316L 316 cold rolled stainless steel coil
Short Description:
316 is a special stainless steel, due to the addition of Mo elements to corrosion resistance, and high temperature strength has greatly improved, high temperature up to 1200-1300 degrees, can be used under harsh conditions.
Sino Stainless Steel Capacity about 316L 316 cold rolled stainless steel coil, 316 316L CRC
Thickness(316L 316 cold rolled stainless steel coil): 0.2mm – 8.0mm
Width(316L 316 cold rolled stainless steel coil): 600mm – 2000mm, the narrowed products pls check in strip products
Max coil weight(316L 316 cold rolled stainless steel coil): 25MT
Coil ID(316L 316 cold rolled stainless steel coil): 508mm,610mm
Finish(316L 316 cold rolled stainless steel coil): 2B,2D
316 Same grade from different country standard(316L 316 cold rolled stainless steel coil):
06Cr17Ni12Mo2 0Cr17Ni12Mo2 S31600 SUS316 1.4401
316 Chemical component ASTM A240 (316L 316 cold rolled stainless steel coil):
C:≤0.08 ,Si :≤0.75 Mn :≤2.0 , S :≤0.03 ,P :≤0.045, Cr :16.0~18.0 ,Ni :10.0~14.0,
Mo: 2.0-3.0, N≤0.1
316 mechanical property ASTM A240 (316L 316 cold rolled stainless steel coil):
Tensile strength : > 515 Mpa
Yield Strength : >205 Mpa
Elongation (%): > 40%
Hardness: < HRB95
316L Same grade from different country standard(316L 316 cold rolled stainless steel coil):
1.4404 022Cr17Ni12Mo2 00Cr17Ni14Mo2 S31603 SUS316L
316L Chemical Component ASTM A240(316L 316 cold rolled stainless steel coil):
C:≤0.03 ,Si :≤0.75 Mn :≤2.0 , S :≤0.03 ,P :≤0.045, Cr :16.0~18.0 ,Ni :10.0~14.0,
Mo: 2.0-3.0, N≤0.1
316L Mechanical Property ASTM A240(316L 316 cold rolled stainless steel coil):
Tensile strength : > 485 Mpa
Yield Strength : >170 Mpa
Elongation (%): > 40%
Hardness: < HRB95
316 Stainless steel coil rolled coil Application
The main uses are paper and papermaking equipment, heat exchangers, dyeing equipment, film processing equipment, pipelines, building exterior materials in coastal areas. also used in the field of solenoid valves, housings, clamps, ball, valve body, seat, nut, stem and so on.
316 stainless steel other features
Corrosion resistance
316 Corrosion resistance is better than 304 stainless steel, in the pulp and paper production process has good corrosion resistance. And 316 stainless steel is also resistant to the erosion of the oceans and the aggressive industrial atmosphere.
Heat resistance
316 stainless steel has good oxidation resistance for intermittent use below 871 ° C (1600 ° F) and continuous use above 927 ° C (1700 ° F). It is best not to continuously use 316 stainless steel in the range of 427 ° C-857 ° C (800 ° F-1575 ° F), but stainless steel possesses excellent heat resistance when 316 stainless steel is continuously used outside this temperature range. 316L stainless steel carbide precipitation performance better than 316 stainless steel, available in the above temperature range.
Heat treatment
Annealing is performed at a temperature in the range of 850-1050 ° C followed by rapid annealing followed by rapid cooling. 316 stainless steel can not be hardened by heat treatment.
316 stainless steel Welding Performance
316 stainless steel with good welding performance. All standard welding methods can be used for welding. Welding can be used according to the purpose, respectively 316Cb, 316L or 309Cb stainless steel filler rods or welding electrodes. In order to obtain the best corrosion resistance, the welded section of 316 stainless steel needs to be annealed after welding. If 316L stainless steel is used, no post-weld annealing is required
316 Stainless Steel Coil
Cold Rolled Stainless Steel Coil
Hot Rolled Stainless Steel Coil
Stainless Steel Coil Stock
Stainless Steel Coil Suppliers
Stainless Steel Coil Tubing
Stainless Steel Pipe Coil