Huaxiao Capacity about 321/321H Hot rolled stainless steel plate ,321/321H HRP,PMP

Description about 321/321H stainless steel

It maintains good resistance to intergranular corrosion at temperatures up to 800-1500 °F (427-816 °C) and chromium carbide precipitation. Due to the addition of titanium to the composition, 321 Hot rolled Stainless steel plate can still maintain stability in the case of chromium carbide formation.

321 Hot rolled Stainless steel plate has advantages in high temperature environment due to its excellent mechanical properties. Compared with 304 alloy, 321 alloy stainless steel has better ductility and resistance to stress fracture. In addition, 304L can also be used for anti-sensitization and intergranular corrosion.

General attribute

Alloy 321 (UNS S32100) is a very stable stainless steel. It maintains good resistance to intergranular corrosion at temperatures up to 800-1500 °F (427-816 °C) and chromium carbide precipitation. Due to the addition of titanium to the composition, 321 Hot rolled Stainless steel plate can still maintain stability in the case of chromium carbide formation. Alloy 347 is due to the addition of niobium and tantalum to maintain its stability. .

Alloys 321 and 347 are commonly used for long-term operation at 800-1500 °F (427-816 °C) in high temperature environments. If the application involves only welding or short-time heating, replace it with 304L.

The high temperature operation advantages of 321 and 347 alloys also depend on their good mechanical properties. Compared with 304, 304L, 321 and 347 have better creep stress and stress crack resistance. This allows the pressure of these stable alloys to meet the American Society of Mechanical Engineering boiler regulations and pressure vessel specifications at a higher temperature. Therefore, the maximum operating temperature of 321 and 347 alloys is 1500 °F (816 °C), while 304, 304L is limited to 800 °F (426 °C).

321 and Alloy 347 also have high carbon content, their UNS numbers are: S32109 and S34709.

Application

It is used in field open-air machines for chemical, coal and petroleum industries with high resistance to intergranular corrosion, heat-resistant parts for building materials and parts with difficult heat treatment, such as:

1. Petroleum waste gas combustion pipeline

2. Engine exhaust pipe

3. Boiler casing, heat exchanger, furnace components

4. Dust-proof parts for diesel engines

5. Boiler pressure vessel

6. Chemical transport vehicles

7. Expansion joint

8. Spiral welded pipe for furnace pipe and dryer

9. Aircraft

Thickness: 1.2mm – 10mm

Width: 600mm – 3200mm, the narrowed products pls check in strip products

Length: 12000mm

Pallet: 1MT – 10MT

Finish: NO.1, 1D, 2D, #1, hot rolled finished, black, Anneal and pickling, mill finish

321 Same grade from different country standard

06Cr18Ni11Ti  0Cr18Ni10Ti  1.4541  SUS321  S32168  S32100  

321 Chemical component  ASTM A240 :

C：≤0.08 ，Si ：≤0.75 　Mn ：≤2.0 ，Cr ：17.0～19.0 ，Ni ：9.0～12.0，　S ：≤0.03 ，P ：≤0.045 N: 0.1 , Ti : 5X(C+N)Min～ 0.70Max

321H Chemical component  ASTM A240 :

C：0.04～0.1 ，Si ：≤0.75 　Mn ：≤2.0 ，Cr ：17.0～19.0 ，Ni ：9.0～12.0，　S ：≤0.03 ，P ：≤0.045 N: 0.1 , Ti : 4X(C+N)Min～ 0.70Max

321/321H  mechanical property ASTM A240 :

Tensile strength :  > 515 Mpa

Yield Strength :  >205 Mpa

Elongation (%):  > 40%

Hardness: < HRB95

Hot Rolled Stainless Steel Plate
Hot rolled Stainless steel plate price