What is the difference between 409 and 410 stainless steel:
409—except for the addition of titanium, the cheapest model, usually used as a car exhaust pipe, is a ferritic stainless steel (chrome steel), suitable for welding, low cost, steam locomotive exhaust pipe, and fire row
410—Martensite (high-strength chrome steel), good wear resistance and poor corrosion resistance, suitable for pumping. Its chemical composition contains 13% chromium, 0.15% or less carbon and a small amount of other elemental alloys. The raw material is cheaper, magnetic, and hardenable by heat treatment. General uses include bearings, medical appliances and tools and appliance panels, and tensile parts.
Huaxiao Capacity about 410 410s Hot rolled stainless steel Plate ,410 410s HRP,PMP
What is the difference between 409 and 410 stainless steel
409—except for the addition of titanium, the cheapest model, usually used as a car exhaust pipe, is a ferritic stainless steel (chrome steel), suitable for welding, low cost, steam locomotive exhaust pipe, and fire row
410—Martensite (high-strength chrome steel), good wear resistance and poor corrosion resistance, suitable for pumping. Its chemical composition contains 13% chromium, 0.15% or less carbon and a small amount of other elemental alloys. The raw material is cheaper, magnetic, and hardenable by heat treatment. General uses include bearings, medical appliances and tools and appliance panels, and tensile parts.
410 430 430F 430LX stainless steel
410 stainless steel is equivalent to China’s 1Cr13 stainless steel S41000 (American AISI, ASTM). 0.01% carbon, 0.13% chromium 0.1 410 stainless steel: good corrosion resistance, machinability, general purpose blades, valves.
Heat treatment of 410 stainless steel: solution treatment (°C) 800-9000 slow cooling or 750 fast cooling
430 stainless steel has good corrosion resistance and general steel grade, thermal conductivity is better than austenite, thermal expansion coefficient is smaller than austenite, heat fatigue, adding stabilizing element titanium, and the mechanical properties of the weld site are good. For building decoration, fuel burner parts, household appliances, home appliances parts.
The 430F is a grade of steel with a free-cutting property on 430 steel. Used in automatic lathes, bolts and nuts.
430LX adds Ti or Nb to 430 steel, lowers C content, and improves processability and weldability. Used in hot water tanks, hot water systems, sanitary appliances, household durable appliances, bicycle flywheels, etc.
410 410s Hot rolled stainless steel Plate product description
Thickness: 1.2mm – 10mm
Width: 600mm – 2000mm, the narrowed products pls check in strip products
Length: 500mm-12000mm
Pallet weight: 40MT
Finish: NO.1, 1D, 2D, #1, hot rolled finished, black, Anneal and pickling, mill finish
410S Same grade from different country standard
S41008 SUS410S
410S Chemical Component :
C:≤0.08,Si :≤1.0 Mn :≤1.0 , S :≤0.03 ,P :≤0.040, Cr :11.5~13.5 ,Ni :0.6 Max,
410s Mechanical Property :
Tensile strength : > 415 Mpa
Yield Strength : >205 Mpa
Elongation (%): > 22%
Hardness: < HRB89
Bending Angle: 180 degree
410 Similar grade from different country standard
S41000 SUS410 1.4006 1.4000 06Cr13 S11306 0Cr13
410 Chemical Component :
C:≤0.08-0.15 ,Si :≤1.0 Mn :≤1.0 , S :≤0.03 ,P :≤0.040, Cr :11.5~13.5 ,Ni :0.75 Max,
410 Mechanical Property :
Tensile strength : > 450 Mpa
Yield Strength : >205 Mpa
Elongation (%): > 20%
Hardness: < HRB96
Bending Angle: 180 degree