06Cr19Ni10 vs 304 Stainless Steel – Which Is Superior?

Stainless steel 06Cr19Ni10 and 304 are both common stainless steel materials and are widely used in various fields. So, 06Cr19Ni10 vs 304 stainless steel – which Is superior? In fact, they have similarities in many aspects, but there are also some subtle differences. Below I will compare the two materials from several perspectives to help you understand their properties, advantages, and disadvantages.

06Cr19Ni10 vs 304 Stainless Steel – Which Is Superior?

06Cr19Ni10 vs 304 Stainless Steel – 1. Chemical composition:

• 06Cr19Ni10:C (carbon) ≤0.08, Si (silicon) ≤1.00, Mn (manganese) ≤2.00, P (phosphorus) ≤0.035, S (sulfur) ≤0.030, Ni (nickel) 8.00-11.00, Cr (chromium) 18.00-20.00.
• 304:C≤0.08, Si≤1.00, Mn≤2.00, P≤0.045, S≤0.030, Ni8.00-10.50, Cr18.00-20.00.

From the chemical composition point of view, the two are very similar, with the main components being carbon, silicon, manganese, phosphorus, sulfur, nickel, and chromium. Therefore, in most cases, their properties and applications are similar.

06Cr19Ni10 vs 304 Stainless Steel – 2. Corrosion resistance:

• 06Cr19Ni10: has good corrosion resistance, with good resistance to most acidic and alkaline media.
• 304: also has excellent corrosion resistance, with good resistance to most common corrosive media.

From the perspective of corrosion resistance, both perform similarly in common corrosive media and can meet general requirements.

06Cr19Ni10 vs 304 Stainless Steel – 3. Strength and mechanical properties:

• 06Cr19Ni10: tensile strength ≥ 520MPa, yield strength ≥ 205MPa, elongation ≥ 40%.
• 304: tensile strength ≥ 515MPa, yield strength ≥ 205MPa, elongation ≥ 35%.

From the perspective of strength and mechanical properties, the two are also very close, both having good strength and plasticity.

06Cr19Ni10 vs 304 Stainless Steel – 4. Magnetic:

• 06Cr19Ni10: It is a non-magnetic material and is not affected by magnetic fields.
• 304: has slight magnetic properties under certain conditions.

From the perspective of magnetic properties, 06Cr19Ni10 has more advantages and is suitable for certain specific application scenarios, such as electronic devices.

Conclusion

Overall, 06Cr19Ni10 and 304 perform similarly in most aspects. Both are common stainless steel materials with good corrosion resistance, strength, and mechanical properties. When selecting, it can be considered based on specific application needs and environmental conditions. If there is a need for magnetic field-sensitive applications, 06Cr19Ni10 may be more suitable. However, in general application scenarios, the performance differences between the two are not significant. Ultimately, which material to choose depends on a comprehensive consideration of factors such as price, supply, and processing based on specific circumstances.

Thank you for reading our article and we hope it can help you to have a better understanding of the difference between 06Cr19Ni10 vs 304 stainless steel. If you want to find more information about 304 stainless steel, we would advise you to visit Sino Stainless Steel for more information.

As a leading supplier of stainless steel products across the world, Sino Stainless Steel provides customers with high-quality stainless steel strips, stainless steel coils, stainless steel plates, stainless steel sheets, stainless steel bars, and stainless steel tubes at an extremely competitive price.